Hostaform® C 9021

聚甲醛（POM）共聚物

Celanese Corporation

產(chǎn)品說明：

Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 03-002

POM copolymer

Standard-Injection molding type with high rigidity, hardness and
toughness; good chemical resistance to solvents, fuel and strong
alkalis as well as good hydrolysis resistance; high resistance to
thermal and oxidative degradation.

Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470

UL-registration for all colours and a thickness more than 1.5 mm as
UL 94 HB, temperature index UL 746 B electrical 110°C, mechanical
90°C.

Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more
than 1 mm.

Ranges of applications: automotive engineering, precision
engineering, electric and electronical industry, domestic
appliances.

FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)

會員資料

公司名稱:

聯(lián)系人:

公司地址:

完善資料

附加功能

PDF物性文檔
[普通版本] [帶會員聯(lián)系方式版本]

查找替代物

黃卡資料

加入收藏

Hostaform® C 9021 物性表

基本信息
黃卡編號	E42337-234607
特性	剛性，高抗溶劑性耐化學(xué)性良好耐堿耐燃油性耐水解性韌性良好硬度高
用途	電氣/電子應(yīng)用領(lǐng)域電器用具工程配件汽車領(lǐng)域的應(yīng)用
機(jī)構(gòu)評級	FDA 21 CFR 177.2470 歐洲 10/1/2011 12:00:00 AM
RoHS 合規(guī)性	聯(lián)系制造商
加工方法	注射成型
多點(diǎn)數(shù)據(jù)	Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1)
樹脂ID (ISO 1043)	POM

物理性能	額定值	單位制	測試方法
密度	1.41	g/cm3	ISO 1183
溶化體積流率（MVR） (190°C/2.16 kg)	8.00	cm3/10min	ISO 1133
收縮率			ISO 294-4
垂直流動方向	1.8	%	ISO 294-4
流動方向	2.0	%	ISO 294-4
吸水率 (飽和, 23°C)	0.65	%	ISO 62

機(jī)械性能	額定值	單位制	測試方法
拉伸模量	2850	MPa	ISO 527-2/1A/1
拉伸應(yīng)力 (屈服)	64.0	MPa	ISO 527-2/1A/50
拉伸應(yīng)變 (屈服)	9.0	%	ISO 527-2/1A/50
標(biāo)稱拉伸斷裂應(yīng)變	30	%	ISO 527-2/1A/50
拉伸蠕變模量			ISO 899-1
1 hr	2500	MPa	ISO 899-1
1000 hr	1300	MPa	ISO 899-1
彎曲模量 (23°C)	2700	MPa	ISO 178

沖擊性能	額定值	單位制	測試方法
簡支梁缺口沖擊強(qiáng)度			ISO 179/1eA
-30°C	6.0	kJ/m2	ISO 179/1eA
23°C	6.5	kJ/m2	ISO 179/1eA
簡支梁無缺口沖擊強(qiáng)度			ISO 179/1eU
-30°C	160	kJ/m2	ISO 179/1eU
23°C, 局部斷裂	180	kJ/m2	ISO 179/1eU

熱性能	額定值	單位制	測試方法
熱變形溫度 (1.8 MPa, 未退火)	104	°C	ISO 75-2/A
熔融溫度 1	166	°C	ISO 11357-3
線形熱膨脹系數(shù)			ISO 11359-2
流動	1.1E-4	cm/cm/°C	ISO 11359-2
橫向	1.1E-4	cm/cm/°C	ISO 11359-2

電氣性能	額定值	單位制	測試方法
表面電阻率	1.0E+14	ohms	IEC 60093
體積電阻率	1.0E+14	ohms·cm	IEC 60093
介電強(qiáng)度	35	kV/mm	IEC 60243-1
相對電容率			IEC 60250
100 Hz	4.00		IEC 60250
1 MHz	4.00		IEC 60250
耗散因數(shù)			IEC 60250
100 Hz	2.0E-3		IEC 60250
1 MHz	5.0E-3		IEC 60250
漏電起痕指數(shù)	600	V	IEC 60112

可燃性	額定值	測試方法
UL 阻燃等級		UL 94
1.50 mm	HB	UL 94
3.00 mm	HB	UL 94

充模分析	額定值	單位制	測試方法
Density of Melt	1.200	g/cm3	內(nèi)部方法
Ejection Temperature	165	°C	內(nèi)部方法
Specific Heat Capacity of Melt	2210	J/kg/°C	內(nèi)部方法
Thermal Conductivity of Melt	0.16	W/m/K	內(nèi)部方法

補(bǔ)充信息	額定值	單位制	測試方法
Effective Thermal Diffusivity	0.0485	cSt	內(nèi)部方法

注射	額定值	單位制
干燥溫度	120 到 140	°C
干燥時間	3.0 到 4.0	hr
建議的最大水分含量	0.15	%
料斗溫度	20.0 到 30.0	°C
料筒后部溫度	170 到 180	°C
料筒中部溫度	180 到 190	°C
料筒前部溫度	190 到 200	°C
射嘴溫度	190 到 210	°C
加工（熔體）溫度	190 到 210	°C
模具溫度	80.0 到 120	°C
注塑壓力	60.0 到 120	MPa
注射速度	慢到中等
保壓	60.0 到 120	MPa
背壓	0.00 到 4.00	MPa