TYPICAL PROPERTIES (1)
|
|
MECHANICAL/機械性能
|
Value/值
|
Unit/單位
|
Standard/標準
|
|
Tensile Stress, yld, Type I / 抗張程度,屈服,類型I, 5 mm/min
|
95
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗張程度,斷裂,類型I, 5 mm/min
|
95
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸長,屈服,類型I, 5 mm/min
|
1.2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸長,斷裂,類型I, 5 mm/min
|
1.2
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 5 mm/min
|
11500
|
MPa
|
ASTM D 638
|
|
Flexural Stress, brk / 彎曲強度,斷裂, 1.3 mm/min, 50 mm span
|
186
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 撓曲模量, 1.3 mm/min, 50 mm span
|
9400
|
MPa
|
ASTM D 790
|
|
Hardness，Rockwell / 洛氏硬度 R
|
119
|
–
|
ASTM D 785
|
|
IMPACT/沖擊性能
|
Value/值
|
Unit/單位
|
Standard/標準
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊, 23°C
|
640
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度, 23°C
|
69
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度, -30°C
|
64
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Total Energy / 裝有測量儀表的落鏢沖擊總能量, 23°C
|
6
|
J
|
ASTM D 3763
|
|
THERMAL/熱性能
|
Value/值
|
Unit/單位
|
Standard/標準
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50
|
200
|
°C
|
ASTM D 1525
|
|
HDT（熱變形溫度）, 0.45 MPa, 3.2 mm, unannealed （未退火）
|
212
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
200
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
215
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
204
|
°C
|
ASTM D 648
|
|
CTE（線形膨脹系數(shù)）, -40°C to 40°C, flow（流動）
|
2.52E-05
|
1/°C
|
ASTM E 831
|
|
CTE（線形膨脹系數(shù)）, 60°C to 138°C, flow（流動）
|
2.52E-05
|
1/°C
|
ASTM E 831
|
|
Relative Temp Index, Elec / 相對熱指數(shù)， 電性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相對熱指數(shù)，機械沖擊性能
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相對熱指數(shù)，非機械沖擊性能
|
140
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值
|
Unit/單位
|
Standard/標準
|
|
Specific Gravity / 比重
|
1.61
|
–
|
ASTM D 792
|
|
Specific Volume / 比容
|
0.62
|
cm3/g
|
ASTM D 792
|
|
Water Absorption / 吸水率, 24 hours
|
0.06
|
%
|
ASTM D 570
|
|
Mold Shrinkage / 收縮率, flow（流動）, 3.2 mm
|
0.5 – 0.7
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, flow（流動）, 1.5-3.2 mm
|
0.3 – 0.5
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, flow（流動）, 3.2-4.6 mm
|
0.5 – 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, xflow（橫向）, 1.5-3.2 mm
|
0.4 – 0.6
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, xflow（橫向）, 3.2-4.6 mm
|
0.6 – 1
|
%
|
SABIC Method
|
|
ELECTRICAL/電氣性能
|
Value/值
|
Unit/單位
|
Standard/標準
|
|
Volume Resistivity / 體積電阻率
|
>3.4E+16
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air / 介電強度，空氣中, 3.2 mm
|
19.2
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in oil / 耐電強度，在油中, 1.6 mm
|
24
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相對介電常數(shù), 100 Hz
|
3.8
|
–
|
ASTM D 150
|
|
Relative Permittivity / 相對介電常數(shù), 1 MHz
|
3.7
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 100 Hz
|
0.002
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.02
|
–
|
ASTM D 150
|
|
Arc Resistance, Tungsten / 耐電弧性 {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 熱絲引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高電壓電弧起痕速率 {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高電流電弧引燃，表面 {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù) (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值
|
Unit/單位
|
Standard/標準
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等級 (3)
|
0.71
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
2
|
mm
|
UL 94
|
|
CSA (See File for complete listing)
|
LS88480
|
File No.
|
CSA LISTED
|
|
Oxygen Index / 極限氧指數(shù) (LOI)
|
32
|
%
|
ASTM D 2863
|
|
UV-light, water exposure/immersion / 紫外線暴露，耐水/浸漬
|
F2
|
–
|
UL 746C
|