性能項目
|
試驗條件[狀態(tài)]
|
測試方法
|
測試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
基本性能
|
密度
|
ASTM D-792
|
|
1.42
|
|
|
物理性能
|
吸水量
|
浸泡均衡點+73℉(+23℃)
|
ASTM D-570
|
1.40
|
%
|
|
吸水量
|
24hrs浸泡+73℉(+23℃)
|
ASTM D-570
|
0.32
|
%
|
|
機(jī)械性能
|
彎曲疲勞忍耐限度
|
+73℉
|
ASTM D-671
|
4.0
|
MPsi
|
|
擴(kuò)散因數(shù)
|
+73℉(+23℃)106Hz
|
ASTM D-150
|
0.005
|
|
|
伸張強度
|
+250℉
|
ASTM D-638
|
3.3
|
MPsi
|
|
斷裂時之拉力伸張度
|
+250℉(+122℃)
|
ASTM D-638
|
>260
|
%
|
|
伸張強度
|
+122℃
|
ASTM D-638
|
22.8
|
MPa
|
|
彎曲疲勞忍耐限度
|
+23℃
|
ASTM D-671
|
27.6
|
MPa
|
|
壓縮應(yīng)力
|
+73℉@1%Def.
|
ASTM D-695
|
4.5
|
MPsi
|
|
伸張強度
|
+158℉
|
ASTM D-638
|
6.6
|
MPsi
|
|
壓縮應(yīng)力
|
+23℃@10%Def.
|
ASTM D-695
|
108
|
MPa
|
|
吸水量
|
Equil.50%R.h.+73℉(+23℃)
|
ASTM D-570
|
0.28
|
%
|
|
彎曲降服強度
|
+73℉
|
ASTM D-790
|
13.6
|
MPsi
|
|
撓曲系數(shù)
|
+73℉
|
在25℃下
|
400
|
MPsi
|
|
IZOD沖擊強度
|
+23℃
|
ASTM D-256
|
69.4
|
j/m
|
|
伸張強度
|
+70℃
|
ASTM D-638
|
45.5
|
MPa
|
|
IZOD沖擊強度
|
40℃
|
ASTM D-256
|
53.4
|
j/m
|
|
伸張強度
|
+23℃
|
ASTM D-638
|
66.9
|
MPa
|
|
伸張強度
|
+212℉
|
ASTM D-638
|
4.3
|
MPsi
|
|
彈性系數(shù)
|
+23℃
|
ASTM D-638
|
3100
|
MPa
|
|
撓曲系數(shù)
|
+212℉
|
在25℃下
|
130
|
MPsi
|
|
伸張強度
|
+73℉
|
ASTM D-638
|
9.7
|
MPsi
|
|
撓曲系數(shù)
|
+23℃
|
在25℃下
|
2760
|
MPa
|
|
伸張強度
|
-68℉
|
ASTM D-638
|
14.0
|
MPsi
|
|
斷裂時之拉力伸張度
|
+212℉(+100℃)
|
ASTM D-638
|
>260
|
%
|
|
彈性系數(shù)
|
+73℉
|
ASTM D-638
|
450
|
MPsi
|
|
伸張強度
|
-55℃
|
ASTM D-638
|
96.5
|
MPa
|
|
剪力
|
+23℃
|
ASTM D-732
|
65.5
|
MPa
|
|
撓曲系數(shù)
|
+70℃
|
在25℃下
|
1515
|
MPa
|
|
伸張強度
|
+100℃
|
ASTM D-638
|
29.6
|
MPa
|
|
撓曲系數(shù)
|
+158℉
|
在25℃下
|
220
|
MPsi
|
|
斷裂時之拉力伸張度
|
+73℉(+23℃)
|
ASTM D-638
|
25
|
%
|
|
撓曲系數(shù)
|
-55℃
|
在25℃下
|
3930
|
MPa
|
|
壓縮應(yīng)力
|
+73℉@10%Def.
|
ASTM D-695
|
15.6
|
MPsi
|
|
撓曲系數(shù)
|
-68℉
|
在25℃下
|
570
|
MPsi
|
|
壓縮應(yīng)力
|
+23℃@1%Def.
|
ASTM D-695
|
31.0
|
MPa
|
|
摩擦系數(shù)
|
+73℉(+23℃)動態(tài)
|
ThrustWasherTest3
|
0.20
|
|
|
負(fù)載下之變形
|
2000psi@+122℉(14Mpa@50℃)
|
ASTM D-621
|
0.7
|
%
|
|
剪力
|
+73℉
|
ASTM D-732
|
9.5
|
MPsi
|
|
IZOD沖擊強度
|
-40℉
|
ASTM D-256
|
1.0
|
ft.lb/in
|
|
彎曲降服強度
|
+23℃
|
ASTM D-790
|
93.8
|
MPa
|
|
撓曲系數(shù)
|
+100℃
|
在25℃下
|
895
|
MPa
|
|
撓曲系數(shù)
|
+122℃
|
在25℃下
|
550
|
MPa
|
|
斷裂時之拉力伸張度
|
+158℉(+70℃)
|
ASTM D-638
|
150
|
%
|
|
IZOD沖擊強度
|
+73℉
|
ASTM D-256
|
1.3
|
ft.lb/in
|
|
電氣性能
|
絕緣強度
|
Short Time,2.3mm
|
ASTM D-149
|
19.7
|
MV/m
|
|
電阻系數(shù)
|
+73℉(+23℃)0.2%H2O
|
ASTM D-257
|
1015
|
ohm-cm
|
|
絕緣系數(shù)
|
+73℉(+23℃)102to106Hz
|
ASTM D-150
|
3.7
|
|
|
電弧抵抗力
|
120mil(3.1mm)
|
ASTM D-495
|
220no tracking
|
Sec.
|
|
絕緣強度
|
Short Time,90 mils
|
ASTM D-149
|
500
|
V/mil
|
|
熱性能
|
線性熱膨脹系數(shù)
|
+220 to +300℉
|
ASTM D-696
|
8.3
|
10-5in/in.℉
|
|
線性熱膨脹系數(shù)
|
+140 to +220℉
|
ASTM D-696
|
7.6
|
10-5in/in.℉
|
|
熱變形溫度
|
0.5MPa
|
ASTM D-648
|
170
|
℃
|
|
熱變形溫度
|
1.8MPa
|
ASTM D-648
|
130
|
℃
|
|
線性熱膨脹系數(shù)
|
+60 to +104℃
|
ASTM D-696
|
13.7
|
10-5m/m.℃
|
|
熔點
|
|
ASTM D-2133
|
347
|
℉
|
|
線性熱膨脹系數(shù)
|
+29 to +60℃
|
ASTM D-696
|
12.2
|
10-5m/m.℃
|
|
線性熱膨脹系數(shù)
|
-40 to +85℉
|
ASTM D-696
|
5.8
|
10-5in/in.℉
|
|
可燃燒性
|
|
UL-94
|
94HB
|
|
|
熔點
|
ASTM D-2133
|
|
175
|
℃
|
|
熱變形溫度
|
66psi
|
ASTM D-648
|
328
|
℉
|
|
線性熱膨脹系數(shù)
|
+104 to +150℃
|
ASTM D-696
|
14.9
|
10-5m/m.℃
|
|
線性熱膨脹系數(shù)
|
-40 to +29℃
|
ASTM D-696
|
10.4
|
10-5m/m.℃
|
|
熱變形溫度
|
264psi
|
ASTM D-648
|
266
|
℉
|
|
線性熱膨脹系數(shù)
|
+85 to +140℉
|
ASTM D-696
|
6.8
|
10-5in/in.
|
|
在線咨詢 