性能項(xiàng)目
|
試驗(yàn)條件[狀態(tài)]
|
測(cè)試方法
|
測(cè)試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
基本性能
|
吸水率
|
24hr,23℃
|
ASTM D-570
|
0.20
|
%
|
|
熔體流動(dòng)速率
|
300℃，1.2kg
|
ASTM D-1238
|
10
|
g/10min
|
|
物理性能
|
濁度
|
3.2mmt
|
ASTM D-1003
|
＜0.8
|
%
|
|
比重
|
23/23℃
|
ASTM D-792
|
1.20
|
|
|
全光穿透率
|
3mmt
|
ASTM D-570
|
89
|
%
|
|
機(jī)械性能
|
曲折率
|
|
ASTM D-542
|
1.585
|
%
|
|
彎曲模數(shù)
|
23℃
|
ASTM D-790
|
24000
|
kg/m2
|
|
壓縮強(qiáng)度
|
|
ASTM D-695
|
780
|
Kg/cm2
|
|
IZOD缺口沖擊強(qiáng)度
|
1/8"
|
ASTM D-256
|
87
|
kg.cm/cm
|
|
彎曲強(qiáng)度
|
23℃
|
ASTM D-790
|
920
|
kg/m2
|
|
洛氏硬度
|
|
ASTM D-785
|
M-77
|
M Scale
|
|
IZOD缺口沖擊強(qiáng)度
|
1/4"
|
ASTM D-256
|
14.3
|
kg.cm/cm
|
|
降伏引張強(qiáng)度
|
23℃
|
ASTM D-638
|
630
|
kg/m2
|
|
延伸率
|
降伏點(diǎn)
|
23℃
|
ASTM D-638
|
6
|
℃
|
|
破裂點(diǎn)
|
23℃
|
ASTM D-638
|
110
|
℃
|
|
電氣性能
|
體積電阻率
|
|
ASTM D-257
|
3
|
×1016Ω.cm
|
|
耐電弧性
|
|
ASTM D-495
|
110
|
Sec
|
|
絕緣破壞強(qiáng)度
|
1.6mm
|
ASTM D-149
|
30
|
KV/mm
|
|
介電損耗
|
60Hz
|
ASTM D-150
|
0.0004
|
|
|
介電常數(shù)
|
60Hz
|
ASTM D-150
|
2.95
|
|
|
介電常數(shù)
|
106Hz
|
ASTM D-150
|
2.9
|
|
|
介電損耗
|
106Hz
|
ASTM D-150
|
0.009
|
|
|
加工性能
|
成型收縮率
|
Parallel
|
ASTM D-955
|
0.5-0.7
|
%
|
|
成型收縮率
|
Across
|
ASTM D-955
|
0.5-0.7
|
%
|
|
熱性能
|
熱傳導(dǎo)系數(shù)
|
|
ASTM C-177
|
0.2
|
W/m℃
|
|
熱變形溫度
|
未退火,18.6Kg/cm2,120℃
|
ASTM D-648
|
125
|
℃
|
|
熱變形溫度
|
未退火,4.6Kg/cm2,120℃
|
ASTM D-648
|
136
|
℃
|
|
線膨脹系數(shù)
|
40～100℃
|
ASTM D-696
|
6-8
|
×10-5cm/cm/℃
|
|
燃燒性
|
1/16"
|
UL 94
|
V-2
|
|
|
維卡軟化點(diǎn)
|
1Kg,50℃/hr
|
ASTM D-1525
|
153
|
℃
|
|