HB-YD114(Q)
|
1.6
|
50-55
(受強烈后
After high impact)
|
高錳鋼堆焊焊絲，受強烈后，表面具有加工硬度的特點。
High-manganese steelhardfacing flux-cored wires, and applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
|
|
HB-YD115(Q)
|
1.6
|
50-55
(受強烈后After high impact)
|
用于受嚴錳鋼堆焊，加工硬化效果顯著。
Applied to repair surface of high impact wear parts, cladding layer is impacted with work hardening.
|
|
HB-YD165(Q)
|
1.6
|
60-65
|
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
|
|
HB-YD172(Q)
|
1.6
|
≥40
|
用于堆焊齒輪、挖泥斗、礦山機械等磨損件
Applied to repair surface of high impact wear parts, such as gear aud bucket and mining machinery.
|
|
HB-YD207(Q)
|
1.6
|
≥50
|
用于堆焊推土機刀片，螺旋槳等磨損零件
Applied to repair surface of high wear parts, such as bulldozer blade and propeller.
|
|
HB-YD212(Q)
|
1.2/1.6
|
≥50
|
用于堆焊各種受磨損的機件表面，如齒輪、挖斗、礦山機械
Applied to repair surface of wear parts, such as gear mud bucket and mining machinery.
|
|
HB-YD256(Q)
|
1.6
|
HB≥170
|
高錳鋼堆焊，適用于破碎機等受磨損部位的堆焊
High-manganese steelhardfacing flux-cored Wires,it is applied to repair surface of high impact wear parts, such as Crusher.
|
|
HB-YD258(Q)
|
1.6
|
55-60
|
用于耐磨表面堆焊
Applied to repair surface of wear parts.
|
|
HB-YD265(Q)
|
1.6
|
60-65
|
高硬度耐磨焊絲，適用于磨粒磨損表面堆焊
High hardness wear-resistant wire, it is used to abrasive wearsurfacing welding.
|
|
HB-YD322(Q)
|
1.6
|
≥55
|
用于堆焊各種沖模及切削刃具，兼用于修復要求耐磨損性能較高之機械零件
Applied to repair surface ofhigh wear resistanceparts, such as die and cuttingcutlery.
|
|
HB-YD327A(Q)
|
1.6
|
≥55
|
專門用于模具堆焊，耐磨性能高于D322
Used tomouldsurfacing, wear resistance is better than D322.
|
|
HB-YD337(Q)
|
1.6
|
≥48
|
用于鑄鋼或鍛鋼上堆焊鍛模
Applied to repairforging dieatcast steelorforging steel.
|
|
HB-YD397(Q)
|
1.6
|
≥40
|
用于堆焊鑄鋼或鍛鋼做坯體的熱鍛；蚨押父邚姸饶湍ゼ
Applied to repair hotforging dieatcast steelor forging steel, or highstrengthwear surfacing.
|
|
HB-YD405A(Q)
|
1.6
|
50-59
|
用于熱軋輥開坯輥堆焊
Applied to repair hot-rolling blooming rollor.
|
|
HB-YD430A(Q)
|
1.6
|
20-35
|
打底層堆焊焊絲
A backing hardfacing flux-cored Wires
|
|
HB-YD488A(Q)
|
1.6
|
45-50
|
用于軋輥堆焊
Applied to repair rollor
|
|
HB-YD507Mo(Q)
|
1.6
|
35-45
|
用于510℃以下中高壓閥門堆焊
Applied to valve which operating tdivperature is less than 510℃.
|
|
HB-YD518(Q)
|
1.6
|
40-50
|
用于連鑄輥堆焊
Applied to repaircontinuous caster roller
|
|
HB-YD688(Q)
|
1.6
|
50-60
|
用于磨煤輥打底焊(韌性好，可以多層堆焊)
Used to coal roller backing welding.
|
|
HB-YD788(Q)
|
1.6
|
55-62
|
硬度高，可以多層堆焊。
High hardness andmulti-layer welding
|
|
HB-YD888(Q)
|
1.2, 1.6
|
60-65
|
硬度高，堆焊層厚度不超過6mm。
High hardness, but thethicknessofsurfacing layeris less than 6mm.
|
|
HB-YD888Ni(Q)
|
1.2
|
58-65
|
高鉻合金焊絲，用于耐磨表面堆焊
Applied to repair surface of wear parts.
|
|
HB-YD988(Q)
|
1.6
|
55-63
|
高鉻合金焊絲，用于耐磨表面堆焊
Applied to repair surface of wear parts.
|
|
HB-YD990(Q)
|
1.6
|
55-65
|
用于高溫耐磨堆焊。
Applied to repair surface ofhigh tdivperaturewear parts.
|
|
HB-YD58(Q)
|
1.6
|
55-60
|
高溫耐磨焊絲，用于化推焦機磨靴的堆焊。
high tdivperaturewear hardfacing wires,
|
|
HB-YD67(Q)
|
1.6
|
58-63
|
用于耐磨表面堆焊
Applied to repair surface of wear parts.
|
|
HB-YD95(Q)
|
1.6
|
55-63
|
高鉻合金焊絲，用于耐磨表面堆焊
Applied to repair surface of wear parts.
|
|
HB-DG7(Q)
|
1.6
|
52-60
|
地鐵盾構施工刀具刃口堆焊專用，也可用于煤碳石裝載機料斗和刃口堆焊修復。
Applied to repair surface of high impact wear parts, such as shiled machine, excavator bucket and hopper of mining machinery products
|